聚酰胺樹脂產品型號 、特性值
型號 | 類別 | 酸值 | 胺值 | 粘度 | 容忍值 | 色澤 | 軟化點 | 備注 |
DMA-8080 | 苯溶 | < 5 | < 5 | 70-90 | / | ≤8 | 105-120 | 粘度和色澤在固體份為40% ,溶劑為二甲苯與異丙醇和無水乙醇(4 :3 :3)時計。粘度測定為旋轉法 。 |
DMA-8100 | 苯溶 | < 5 | < 5 | 90-110 | / | ≤8 | 105-115 | |
DMA-8120 | 苯溶 | < 5 | < 5 | 110-140 | / | ≤8 | 105-115 | |
DMA-8150 | 苯溶 | < 5 | < 5 | 140-160 | / | ≤8 | 105-115 | |
DMA-8200 | 苯溶 | < 5 | < 5 | 160-260 | / | ≤8 | 105-115 | |
DMA-8528 | 苯溶 | < 6 | < 6 | 100-160 | / | ≤8 | 105-115 | |
DMA-8066L | 苯溶 | < 5 | < 5 | 80-120 | / | ≤8 | 105-120 | |
DMA-8066 | 苯溶 | < 5 | < 5 | 120-160 | / | ≤8 | 105-115 | |
DMA-8066H | 苯溶 | < 5 | < 5 | 160-220 | / | ≤8 | 105-115 | |
DMA-8060 | 苯溶 | <6 | <6 | C-E | / | ≤8 | 106-115 | 粘度和色澤在固體份為40% ,溶劑為甲苯與異丙醇(7 :3)時計 。粘度測定為氣泡法 。
|
DMA-8074 | 苯溶 | <6 | <6 | E-G | / | ≤8 | 106-115 | |
DMA-8074H | 苯溶 | <6 | <6 | G-H | / | ≤8 | 106-115 | |
DMA-8370 | 苯溶 | <6 | <6 | C-F | / | ≤8 | 95-105 | |
DMA-8094 | 苯溶 | <6 | <6 | E-G | / | ≤10 | 100-120 | |
DMA-8104 | 苯溶 | <6 | <6 | J-M | / | ≤10 | 110-122 | |
DMC-9155 | 醇溶 | <6 | <6 | C-F | >6.7g | ≤10 | 110-125 | 粘度和色澤在固體份為50% ,溶劑為95%乙醇時計 。粘度測定為氣泡法。
|
DMC-9433 | 醇溶 | <6 | <6 | E-G | >4.3g | ≤10 | 117-127 | |
DMC-9399 | 醇溶 | <6 | <6 | F-H | >0.5g | ≤10 | 115-125 | |
DMC-9584 | 醇溶 | <6 | <6 | F-H | >1.1g | ≤10 | 112-124 | |
DMC-9011 | 醇溶 | <4 | <6 | E-H | >6.5g | ≤10 | 97-105 | |
DMC-9445 | 醇溶 | <6 | <6 | F-H | >6.0g | ≤10 | 140-150 | |
DMC-9243 | 醇溶 | <10 | <10 | W-Y | ≤10 | 140-150 | ||
DMC-9084 | 醇溶 | <15 | <15 | C-G | ≤16 | 175-200 |